Francesco Iacoviello Vittorio Di Cocco Mauro Cavallini

Abstract

Microstructure influence on fatigue crack propagation resistance in five different ductile cast irons
(DCI) was investigated. Four ferrite/pearlite volume fractions were considered, performing fatigue crack
propagation tests according to ASTM E647 standard (R equals to 0.1, 0.5 and 0.75, respectively). Results were
compared with an austempered DCI. Damaging micromechanisms were investigated according to the following
procedures:
- “traditional” Scanning Electron Microscope (SEM) fracture surfaces analysis;
- SEM fracture surface analysis with 3D quantitative analysis;
- SEM longitudinal crack profile analysis
- Light Optical Microscope (LOM) transversal crack profile analysis;

Comments

  1. Latest Oldest Top Comments

    ##plugins.themes.bootstrap3.article.details##

    Section
    Articles

    How to Cite

    Iacoviello, F., Di Cocco, V. and Cavallini, M. (2013) “Ductile cast irons: microstructure influence on fatigue crack propagation resistance”, Frattura ed Integrità Strutturale, 4(13), pp. pages 3–16. doi: 10.3221/IGF-ESIS.13.01.